Objective:

To determine the effect of the intensity of two light curing units on the biocompatibility, flexural strength and elastic modulus of a composite resin.

Methodology:

Two groups of Filtek Z250XT (3M ESPE) composite resin were created, each one photopolymerized using different intensities (<400 mW/cm2 for 40s and> 800 mW/cm2 for 20s). Cell viability was analyzed by MTT assay at 24 and 48 hours following the ISO 10993-5 standard. The flexural strength and elastic modulus were analyzed following the ISO 4049 standard.

Results:

In the group photopolymerized with an intensity <400 mW/cm2, cytotoxicity was statistically higher both at 24 and 48 hours and flexural strength and elastic modulus were statistically lower.

Conclusion:

A polymerization intensity <400 mW/cm2 increases the levels of cytotoxicity and decreases the mechanical properties of composite resins. The importance of the periodic control of the light curing units is emphasized.